- 熔体流动速率 [g/10min]: 5.0
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.26
- 拉伸强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 2.05
- 硬度: 70.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C | 5.0 g/10 min @Load 11.0 lb, Temperature 392 °F | Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Tensile Modulus | 2.14 GPa | 310 ksi | ASTM D638 |
| Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
| Flexural Modulus | 2.05 GPa | 297 ksi | ASTM D790 |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.0 J/cm | 18.7 ft-lb/in | ASTM D256 |
| Gardner Impact | 11.0 J | 8.11 ft-lb | Geometry GB; ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | ASTM D1003 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 179 - 213 °C | 354 - 415 °F | |
| Middle Barrel Temperature | 185 - 218 °C | 365 - 424 °F | |
| Front Barrel Temperature | 191 - 224 °C | 376 - 435 °F | |
| Melt Temperature | 204 - 238 °C | 399 - 460 °F | |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Back Pressure | 0.689 MPa | 100 psi | |