- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.16
- 缺口冲击强度: 0.534
- 透光率 [%]: 91.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Melt Flow | 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 4.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 50.3 MPa | 7300 psi | ASTM D638 |
| Elongation at Break | 38 % | 38 % | ASTM D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Gardner Impact | 3.62 J | 2.67 ft-lb | Falling Weight; ASTM D3029GB |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.9 °C | 174 °F | ASTM D648 |
| Vicat Softening Point | 112 °C | 233 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 91.3 % | 91.3 % | Luminous Transmittance; ASTM D1003 |