- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.694
- 断裂伸长率 [%]: 118
- 弯曲模量 [MPa]: 3.52
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Melt Flow | 0.90 g/10 min @Load 3.80 kg, Temperature 230 °C | 0.90 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 84.1 MPa | 12200 psi | ASTM D638 |
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Flexural Modulus | 3.52 GPa | 510 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 6.35 mm | 1.30 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | 0.25 inch; ASTM D648 |