- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 72.0
- 断裂伸长率 [%]: 110
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 96 | 96 | Method A; ASTM D785 |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| 0.200 J/cm @Temperature -18.0 °C | 0.375 ft-lb/in @Temperature -0.400 °F | ASTM D256 | |
| Gardner Impact | 0.500 J | 0.369 ft-lb | reported as J/cm; ASTM D3029-GB, unpainted |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 µm/m-°C @Temperature -18.0 - 38.0 °C | 30.0 µin/in-°F @Temperature -0.400 - 100 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | annealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Optimal Thermoforming temperature for sheet 0.25-1.0 cm (0.10-0.39 in) |