- 熔体流动速率 [g/10min]: 14.0
- 缺口冲击强度: 0.981
- 断裂伸长率 [%]: 72.6
- 弯曲模量 [MPa]: 2.29
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 53.9 MPa | 7820 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Yield Strength | 72.6 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 2.29 GPa | 333 ksi | ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 3.17 mm | 1.84 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |