- 密度 [g/cm3]: 1.19
- 透光率 [%]: 93.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 175 MPa | 25400 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527-2 | ||
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-2 | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527-2 | ||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 | ||
| Charpy Impact Unnotched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 - 5.00e+15 ohm-cm | 1.00e+15 - 5.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 3.00e+15 - 3.00e+16 ohm | 3.00e+15 - 3.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 2.7 @Frequency 1e+6 Hz | 2.7 @Frequency 1e+6 Hz | |||
| 2.7 @Frequency 50 Hz | 2.7 @Frequency 50 Hz | ||||
| 3.1 @Frequency 1000 Hz | 3.1 @Frequency 1000 Hz | ||||
| Dielectric Strength | 30.0 kV/mm @Thickness 1.00 mm | 762 kV/in @Thickness 0.0394 in | DIN 53481 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | DIN 53752 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 | ||
| Vicat Softening Point | 105 °C | 221 °F | ISO 306 | ||
| Decomposition Temperature | >= 280 °C | >= 536 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.492 | 1.492 | ISO 489 | ||
| Haze | 0.60 % | 0.60 % | AKRYLON XT clear; ISO 14782 | ||
| Transmission, Visible | 93 % @Thickness 3.00 mm | 93 % @Thickness 0.118 in | ISO 1183 | ||
| Descriptive Properties | |||||
| Combustibility Grade | E | EN 13501-1 | |||
| Electrical Strength, kV/mm² | 10 | IEC 60243-1 | |||