- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.99
- 缺口冲击强度: 0.502
- 拉伸强度 [MPa]: 37.0
- 弯曲模量 [MPa]: 1.60
- 硬度: 94.0
- 热变形温度 [℃]: 91.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Flexural Strength | 43.0 MPa | 6240 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.1 °C | 196 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm | V-0 @Thickness 0.0625 in | UL File #E99379(N) |