- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.952
- 缺口冲击强度: 6.51
- 拉伸强度 [MPa]: 16.0
- 弯曲模量 [MPa]: 0.6998
- 硬度: 55.0
- 热变形温度 [℃]: 67.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 0.8998 GPa | 130.5 ksi | ASTM D638 |
| Flexural Strength | 17.0 MPa | 2470 psi | ASTM D790 |
| Flexural Modulus | 0.6998 GPa | 101.5 ksi | ASTM D790 |
| Izod Impact, Notched | 6.51 J/cm | 12.2 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.1 °C | 115 °F | |