- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.112
- 缺口冲击强度: 0.448
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 1.800
- 硬度: 88.0
- 热变形温度 [℃]: 110.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.112 g/cc | 0.04017 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 88 | 88 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.099 GPa | 304.5 ksi | ASTM D638 |
| Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
| Flexural Modulus | 1.800 GPa | 261.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.448 J/cm | 0.840 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.2 °C | 144 °F | |