- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 0.587
- 拉伸强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 4.000
- 硬度: 85.0
- 热变形温度 [℃]: 158.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.299 GPa | 478.5 ksi | ASTM D638 |
| Flexural Strength | 69.98 MPa | 10150 psi | ASTM D790 |
| Flexural Modulus | 4.000 GPa | 580.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | |