- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 1.01
- 拉伸强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 3.000
- 硬度: 33.0
- 热变形温度 [℃]: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 33 | 33 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 2.499 GPa | 362.5 ksi | ASTM D638 |
| Flexural Strength | 22.0 MPa | 3190 psi | ASTM D790 |
| Flexural Modulus | 3.000 GPa | 435.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | |