- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.03
- 缺口冲击强度: 0.502
- 拉伸强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 2.40
- 硬度: 74.0
- 热变形温度 [℃]: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 74 | 74 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 18 % | 18 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ASTM D638 |
| Flexural Strength | 41.0 MPa | 5950 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C | 153 °F | |