- 熔体流动速率 [g/10min]: 17.0
- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 0.299
- 拉伸强度 [MPa]: 30.0
- 弯曲模量 [MPa]: 4.999
- 硬度: 60.0
- 热变形温度 [℃]: 124.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.900 GPa | 565.6 ksi | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 4.999 GPa | 725.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.1 °C | 178 °F | |