- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 1.23
- 缺口冲击强度: 0.801
- 拉伸强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 2.699
- 硬度: 50.0
- 热变形温度 [℃]: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | MD; ASTM D955 |
| Melt Flow | 11 g/10 min | 11 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 50 | 50 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 18 % | 18 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.699 GPa | 391.5 ksi | ASTM D638 |
| Flexural Strength | 26.0 MPa | 3770 psi | ASTM D790 |
| Flexural Modulus | 2.699 GPa | 391.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | |