- 熔体流动速率 [g/10min]: 17.0
- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 1.39
- 拉伸强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 1.60
- 硬度: 53.0
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 53 | 53 | ASTM D785 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Strength | 19.0 MPa | 2760 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.1 °C | 133 °F | |