- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 3.4
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 1.85
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
Filler Content | 30 % | 30 % | ISO 3451 / 1 |
Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 230 °C | 15 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 73 | 73 | ISO 868 |
Tensile Strength, Yield | 23.0 MPa | 3340 psi | ISO 527 |
Elongation at Break | 45 % | 45 % | ISO 527 |
Elongation at Yield | 7.0 % | 7.0 % | ISO 527 |
Flexural Modulus | 1.85 GPa | 268 ksi | ISO 178 |
Izod Impact, Notched (ISO) | 3.40 kJ/m² | 1.62 ft-lb/in² | ISO 180/1A |
Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1U |
Thermal Properties | Metric | English | Comments |
Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75 |
Vicat Softening Point | 94.0 °C | 201 °F | 49 N; ISO 306 |