- 熔体流动速率 [g/10min]: 5.0
- 缺口冲击强度: 0.534
- 拉伸强度 [MPa]: 25.2
- 弯曲模量 [MPa]: 1.93
- 硬度: 87.0
- 热变形温度 [℃]: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Melt Flow | 5.0 g/10 min @Temperature 230 °C | 5.0 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 87 | 87 | ASTM D785 |
| Tensile Strength, Yield | 25.2 MPa | 3650 psi | 2 in/min; ASTM D638 |
| Elongation at Yield | 40 % | 40 % | at max load; ASTM D638 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.7 J/cm | 20.0 ft-lb/in | ASTM D256 |
| Gardner Impact | 7.23 J | 5.33 ft-lb | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.9 °C | 156 °F | ASTM D648 |