- 熔体流动速率 [g/10min]: 8.0
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 35.8
- 弯曲模量 [MPa]: 1.653
- 热变形温度 [℃]: 101.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.903 g/cc | 0.903 g/cc | ASTM D792 |
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Modulus | 1.653 GPa | 239.8 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.267 J/cm | >= 0.500 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 101 °C | >= 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 60.0 °C | >= 140 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |