- 拉伸强度 [MPa]: 27.6
- 弯曲模量 [MPa]: 1.10
- 硬度: 80.0
- 热变形温度 [℃]: 87.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.902 g/cc | 0.902 g/cc | method B; ASTM D792 |
| Melt Index of Compound | 0.45 g/10 min | 0.45 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | .05 in/min, 1% Secant; ASTM D790 |
| Izod Impact, Notched | NB @Temperature 22.8 °C | NB @Temperature 73.0 °F | Method A; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |