- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.905
- 拉伸强度 [MPa]: 22.99
- 热变形温度 [℃]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.99 MPa | 3335 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 5.3 % | 5.3 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.20 GPa | 174 ksi | At 1 mm/min; ISO 527-2 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA |
| 0.700 J/cm² @Temperature -20.0 °C | 3.33 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |
| Impact Test | 35.0 J | 25.8 ft-lb | Total Penetration Energy at 0°C; ISO 6603-2 |
| 40.0 J | 29.5 ft-lb | Total Penetration Energy at -20°C; ISO 6603-2 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |