- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.9
- 弯曲模量 [MPa]: 0.400
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in³ | ISO 1183 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 600 % | 600 % | ISO 527-3 |
| Film Elongation at Break, TD | 900 % | 900 % | ISO 527-3 |
| Flexural Modulus | 0.400 GPa | 58.0 ksi | ISO 178 |
| Secant Modulus, MD | 0.350 GPa | 50.8 ksi | ISO 527-3 |
| Secant Modulus, TD | 0.450 GPa | 65.3 ksi | ISO 527-3 |
| Impact | 62.5 | 62.5 | Dynatest, Damaging Force (N); ISO 7765-2 |
| Impact Test | 0.750 J | 0.553 ft-lb | Dynatest, Penetration Energy; ISO 7765-2 |
| Film Tensile Strength at Break, MD | 45.0 - 65.0 MPa | 6530 - 9430 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 40.0 - 60.0 MPa | 5800 - 8700 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 138 - 142 °C | 280 - 288 °F | ISO 3146 |
| Vicat Softening Point | 110 °C | 230 °F | 10 N; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 50 % | 50 % | ASTM D1003 |
| Gloss | 3.0 % | 3.0 % | At 20°C; ASTM D2457 |