- 熔体流动速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.05
- 拉伸强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 1.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Borealis Method |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C | 13 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 17.00 MPa | 2465 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 70 % | 70 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 1.50 GPa | 218 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² @Temperature -20.0 °C | 2.38 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 µm/m-°C @Temperature -30.0 - 80.0 °C | 33.3 µin/in-°F @Temperature -22.0 - 176 °F | Borealis Method |
| Shrinkage | 0.10 % | 0.10 % | Post Shrinkage at 90°C for 2 hrs.; Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |