- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.04
- 拉伸强度 [MPa]: 24.99
- 弯曲模量 [MPa]: 2.25
- 热变形温度 [℃]: 112.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Borealis Method | ||
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 59.0 MPa | 8560 psi | H385/30; ISO 2039 | ||
| Tensile Strength, Yield | 24.99 MPa | 3625 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | At 50 mm/min; ISO 527-2 | ||
| Flexural Modulus | 2.25 GPa | 326 ksi | At 5 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 3.30 J/cm² @Temperature -40.0 °C | 15.7 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eU | |||
| 3.70 J/cm² @Temperature -20.0 °C | 17.6 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA | ||
| 0.250 J/cm² @Temperature -20.0 °C | 1.19 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.4 °C | 141 °F | ISO 75-2 | ||
| Vicat Softening Point | 80.0 °C | 176 °F | B (50N); ISO 306 | ||
| 150 °C | 302 °F | A (10N); ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 10 | VDA 277 | |||
| Fogging % | 958.2 | At 100°C/3 hours | |||
| Fogging, mg | 0.5 | At 100°C/ 16 hours | |||