- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | H 385/30; ISO 2039 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 2.00 GPa | 290 ksi | At 5 mm/min; ISO 178 |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ISO 75-2 |
| Vicat Softening Point | 158 °C | 316 °F | A (10N); ISO 306 |
| Optical Properties | Metric | English | Comments |
| Gloss | 82 % @Thickness 2.00 mm | 82 % @Thickness 0.0787 in | 20°, plaque; DIN 67530 |
| 90 % @Thickness 2.00 mm | 90 % @Thickness 0.0787 in | 60°, 2 mm plaque; DIN 67530 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |