- 熔体流动速率 [g/10min]: 11.0
- 密度 [g/cm3]: 0.9
- 弯曲模量 [MPa]: 0.600
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.600 g/cc | 0.0181 - 0.0217 lb/in³ | |
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C | 11 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Slip Level | 2000 ppm | 2000 ppm | EAA; Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 - 750 % | 550 - 750 % | ISO 527-3 |
| Tensile Modulus | 0.300 - 0.400 GPa | 43.5 - 58.0 ksi | ISO 527-3 |
| Flexural Modulus | 0.600 GPa | 87.0 ksi | 50% humidity; ISO 178 |
| Dart Drop, Total Energy | 25.0 J @Thickness 0.0500 mm | 18.4 ft-lb @Thickness 0.00197 in | 1200N; ISO 7765-2 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | film to film; ISO 8295 |
| Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 136 - 140 °C | 277 - 284 °F | DSC; ISO 3146 |
| Vicat Softening Point | 120 °C @Load 1.02 kg | 248 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.8 % | <= 1.8 % | ASTM D1003 |
| Gloss | >= 130 % | >= 130 % | 20° of arc; ASTM D2457 |
| Component Elements Properties | Metric | English | Comments |
| SiO2 | 0.18 % | 0.18 % | Antiblock; Borealis Method |