- 熔体流动速率 [g/10min]: 22.5
- 密度 [g/cm3]: 1.07
- 缺口冲击强度: 2.1
- 拉伸强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 3.20
- 热变形温度 [℃]: 120.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Borealis Method; average process | ||
| Melt Flow | 22.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 22.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 93.0 MPa | 13500 psi | 132N/10s; ISO 2039 | ||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 13 % | 13 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 3.10 GPa | 450 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 56.0 MPa | 8120 psi | ISO 178 | ||
| Flexural Modulus | 3.20 GPa | 464 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 2.10 kJ/m² @Temperature -20.0 °C | 0.999 ft-lb/in² @Temperature -4.00 °F | ISO 180/1A | ||
| 4.00 kJ/m² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 1.50 J/cm² @Temperature -20.0 °C | 7.14 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | ||
| 3.80 J/cm² @Temperature 23.0 °C | 18.1 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.0600 J/cm² @Temperature -30.0 °C | 0.286 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.120 J/cm² @Temperature -20.0 °C | 0.571 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | |||
| 0.250 J/cm² @Temperature 23.0 °C | 1.19 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 56.0 µm/m-°C | 31.1 µin/in-°F | (-30°C/80°C); Borealis Method | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ISO 75-2 | ||
| Vicat Softening Point | 97.0 °C @Load 5.10 kg | 207 °F @Load 11.2 lb | ISO 306 | ||
| 154 °C @Load 1.02 kg | 309 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Fogging (mg) | 0.5 | 100°C, 16h; DIN 75201 | |||
| Screw Speed | low to medium | ||||