- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.18
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | average process; in flow; 150x80x2mm | ||
| 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | average process; cross flow; 150x80x2mm | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 118 MPa | 17100 psi | ISO 527-2 | ||
| Elongation at Break | 2.8 % | 2.8 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 | ||
| Flexural Modulus | 8.00 GPa | 1160 ksi | 2mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -20.0 °C | 4.76 ft-lb/in² @Temperature -4.00 °F | ISO 180/1A | ||
| 11.0 kJ/m² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 5.40 J/cm² @Temperature -20.0 °C | 25.7 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eU | ||
| 5.80 J/cm² @Temperature 23.0 °C | 27.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 309 °F | ISO 75-2 | ||
| Vicat Softening Point | 142 °C @Load 5.10 kg | 288 °F @Load 11.2 lb | ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 1667 - 3333 mm/sec | 65.63 - 131.2 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||