- 熔体流动速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.886
- 缺口冲击强度: 0.2
- 拉伸强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.28
- 硬度: 79.0
- 热变形温度 [℃]: 99.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in³ | ASTM D1505 | ||
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 | ||
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 | ||
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 79 - 108 | 79 - 108 | Normal range for injection molding resins; ASTM D785 | ||
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 | ||
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 | ||
| Elongation at Yield | 11 % | 11 % | ASTM D638 | ||
| Flexural Modulus | 1.28 GPa | 186 ksi | ASTM D790A | ||
| Izod Impact, Notched | 0.200 - 0.300 J/cm @Diameter 3.17 mm | 0.375 - 0.562 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Process | Oriented Film/Blow Molding/Fiber | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.