- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.886
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 1.34
- 硬度: 75.0
- 热变形温度 [℃]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in³ | ASTM D1505 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 75 | 75 | ASTM D785 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 1.34 GPa | 194 ksi | ASTM D790A |
| Izod Impact, Notched | NB @Diameter 3.17 mm | NB @Diameter 0.125 in | bar; ASTM D256 |
| 1.35 J/cm @Diameter 3.17 mm, Temperature -20.0 °C | 2.53 ft-lb/in @Diameter 0.125 in, Temperature -4.00 °F | bar; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 120 °C | 248 °F | UL Relative Thermal Index |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |