- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.886
- 缺口冲击强度: 1.35
- 拉伸强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 1.45
- 硬度: 88.0
- 热变形温度 [℃]: 107.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in³ | ASTM D1505 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 88 | 88 | ASTM D785 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 |
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790A |
| Izod Impact, Notched | 1.35 J/cm @Diameter 3.17 mm | 2.53 ft-lb/in @Diameter 0.125 in | bar; ASTM D256 |
| 0.300 J/cm @Diameter 3.17 mm, Temperature -20.0 °C | 0.562 ft-lb/in @Diameter 0.125 in, Temperature -4.00 °F | bar; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ASTM D648 |