  4. Celanese Zenite® FG7145L BK011 LCP

Celanese Zenite® FG7145L BK011 LCP

Celanese Zenite® FG7145L BK011 LCP 物性表: Celanese Zenite® FG7145L BK011 LCP物性表及特性介绍,Celanese Zenite® FG7145L BK011 LCP注塑参数详情,如需Celanese Zenite® FG7145L BK011 LCP下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.74
  • 弯曲模量 [MPa]: 5.00
 
Physical PropertiesMetricEnglishComments
Density 1.74 g/cc0.0629 lb/in³ISO 1183
Filler Content 45 %45 %
Linear Mold Shrinkage, Flow 0.00050 cm/cm
@Thickness 2.00 mm		0.00050 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
@Thickness 2.00 mm		0.0050 in/in
@Thickness 0.0787 in		ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  20.0 MPa
@Thickness 4.00 mm,
Temperature 250 °C		2900 psi
@Thickness 0.157 in,
Temperature 482 °F		ISO 527
 25.0 MPa
@Thickness 2.00 mm,
Temperature 250 °C		3630 psi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 527
 30.0 MPa
@Thickness 4.00 mm,
Temperature 200 °C		4350 psi
@Thickness 0.157 in,
Temperature 392 °F		ISO 527
 30.0 MPa
@Thickness 1.00 mm,
Temperature 250 °C		4350 psi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 527
 35.0 MPa
@Thickness 2.00 mm,
Temperature 200 °C		5080 psi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 527
 40.0 MPa
@Thickness 4.00 mm,
Temperature 150 °C		5800 psi
@Thickness 0.157 in,
Temperature 302 °F		ISO 527
 40.0 MPa
@Thickness 1.00 mm,
Temperature 200 °C		5800 psi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 527
 45.0 MPa
@Thickness 2.00 mm,
Temperature 150 °C		6530 psi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 527
 45.0 MPa
@Thickness 4.00 mm,
Temperature 120 °C		6530 psi
@Thickness 0.157 in,
Temperature 248 °F		ISO 527
 50.0 MPa
@Thickness 2.00 mm,
Temperature 120 °C		7250 psi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 527
 50.0 MPa
@Thickness 1.00 mm,
Temperature 150 °C		7250 psi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 527
 55.0 MPa
@Thickness 1.00 mm,
Temperature 120 °C		7980 psi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 527
 120 MPa
@Thickness 4.00 mm,
Temperature 23.0 °C		17400 psi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 527
 130 MPa
@Thickness 2.00 mm,
Temperature 23.0 °C		18900 psi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 527
 140 MPa
@Thickness 1.00 mm,
Temperature 23.0 °C		20300 psi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 527
 150 MPa
@Thickness 4.00 mm,
Temperature -30.0 °C		21800 psi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 527
 160 MPa
@Thickness 4.00 mm,
Temperature -40.0 °C		23200 psi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 527
 165 MPa
@Thickness 2.00 mm,
Temperature -30.0 °C		23900 psi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 527
 180 MPa
@Thickness 1.00 mm,
Temperature -30.0 °C		26100 psi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 527
 180 MPa
@Thickness 2.00 mm,
Temperature -40.0 °C		26100 psi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 527
 190 MPa
@Thickness 1.00 mm,
Temperature -40.0 °C		27600 psi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 527
Elongation at Break  0.30 %
@Thickness 1.00 mm,
Temperature 250 °C		0.30 %
@Thickness 0.0394 in,
Temperature 482 °F		ISO 527
 0.30 %
@Thickness 1.00 mm,
Temperature 200 °C		0.30 %
@Thickness 0.0394 in,
Temperature 392 °F		ISO 527
 0.40 %
@Thickness 1.00 mm,
Temperature 120 °C		0.40 %
@Thickness 0.0394 in,
Temperature 248 °F		ISO 527
 0.40 %
@Thickness 1.00 mm,
Temperature 150 °C		0.40 %
@Thickness 0.0394 in,
Temperature 302 °F		ISO 527
 0.60 %
@Thickness 4.00 mm,
Temperature 120 °C		0.60 %
@Thickness 0.157 in,
Temperature 248 °F		ISO 527
 0.60 %
@Thickness 4.00 mm,
Temperature 250 °C		0.60 %
@Thickness 0.157 in,
Temperature 482 °F		ISO 527
 0.60 %
@Thickness 2.00 mm,
Temperature 200 °C		0.60 %
@Thickness 0.0787 in,
Temperature 392 °F		ISO 527
 0.60 %
@Thickness 1.00 mm,
Temperature -30.0 °C		0.60 %
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 527
 0.60 %
@Thickness 1.00 mm,
Temperature 23.0 °C		0.60 %
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 527
 0.60 %
@Thickness 4.00 mm,
Temperature 150 °C		0.60 %
@Thickness 0.157 in,
Temperature 302 °F		ISO 527
 0.60 %
@Thickness 1.00 mm,
Temperature -40.0 °C		0.60 %
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 527
 0.70 %
@Thickness 4.00 mm,
Temperature 200 °C		0.70 %
@Thickness 0.157 in,
Temperature 392 °F		ISO 527
 0.70 %
@Thickness 2.00 mm,
Temperature 250 °C		0.70 %
@Thickness 0.0787 in,
Temperature 482 °F		ISO 527
 0.70 %
@Thickness 2.00 mm,
Temperature 120 °C		0.70 %
@Thickness 0.0787 in,
Temperature 248 °F		ISO 527
 0.70 %
@Thickness 2.00 mm,
Temperature 150 °C		0.70 %
@Thickness 0.0787 in,
Temperature 302 °F		ISO 527
 0.90 %
@Thickness 2.00 mm,
Temperature -40.0 °C		0.90 %
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 527
 0.90 %
@Thickness 4.00 mm,
Temperature -40.0 °C		0.90 %
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 527
 0.90 %
@Thickness 4.00 mm,
Temperature -30.0 °C		0.90 %
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 527
 0.90 %
@Thickness 4.00 mm,
Temperature 23.0 °C		0.90 %
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 527
 0.90 %
@Thickness 2.00 mm,
Temperature 23.0 °C		0.90 %
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 527
 0.90 %
@Thickness 2.00 mm,
Temperature -30.0 °C		0.90 %
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 527
Tensile Modulus  6.00 GPa
@Thickness 4.00 mm,
Temperature 250 °C		870 ksi
@Thickness 0.157 in,
Temperature 482 °F		ISO 527
 7.00 GPa
@Thickness 2.00 mm,
Temperature 250 °C		1020 ksi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 527
 7.50 GPa
@Thickness 1.00 mm,
Temperature 250 °C		1090 ksi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 527
 9.00 GPa
@Thickness 4.00 mm,
Temperature 200 °C		1310 ksi
@Thickness 0.157 in,
Temperature 392 °F		ISO 527
 10.0 GPa
@Thickness 2.00 mm,
Temperature 200 °C		1450 ksi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 527
 11.0 GPa
@Thickness 4.00 mm,
Temperature 150 °C		1600 ksi
@Thickness 0.157 in,
Temperature 302 °F		ISO 527
 11.0 GPa
@Thickness 1.00 mm,
Temperature 200 °C		1600 ksi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 527
 11.5 GPa
@Thickness 2.00 mm,
Temperature 150 °C		1670 ksi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 527
 12.0 GPa
@Thickness 1.00 mm,
Temperature 150 °C		1740 ksi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 527
 12.0 GPa
@Thickness 4.00 mm,
Temperature 120 °C		1740 ksi
@Thickness 0.157 in,
Temperature 248 °F		ISO 527
 12.5 GPa
@Thickness 2.00 mm,
Temperature 120 °C		1810 ksi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 527
 13.0 GPa
@Thickness 1.00 mm,
Temperature 120 °C		1890 ksi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 527
 18.0 GPa
@Thickness 4.00 mm,
Temperature 23.0 °C		2610 ksi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 527
 20.5 GPa
@Thickness 2.00 mm,
Temperature 23.0 °C		2970 ksi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 527
 22.0 GPa
@Thickness 1.00 mm,
Temperature 23.0 °C		3190 ksi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 527
 23.5 GPa
@Thickness 4.00 mm,
Temperature -30.0 °C		3410 ksi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 527
 24.5 GPa
@Thickness 4.00 mm,
Temperature -40.0 °C		3550 ksi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 527
 24.5 GPa
@Thickness 2.00 mm,
Temperature -30.0 °C		3550 ksi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 527
 25.0 GPa
@Thickness 1.00 mm,
Temperature -30.0 °C		3630 ksi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 527
 26.0 GPa
@Thickness 2.00 mm,
Temperature -40.0 °C		3770 ksi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 527
 27.0 GPa
@Thickness 1.00 mm,
Temperature -40.0 °C		3920 ksi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 527
Flexural Strength  10.0 MPa
@Thickness 4.00 mm,
Temperature 250 °C		1450 psi
@Thickness 0.157 in,
Temperature 482 °F		ISO 178
 20.0 MPa
@Thickness 2.00 mm,
Temperature 250 °C		2900 psi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 178
 30.0 MPa
@Thickness 1.00 mm,
Temperature 250 °C		4350 psi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 178
 45.0 MPa
@Thickness 4.00 mm,
Temperature 200 °C		6530 psi
@Thickness 0.157 in,
Temperature 392 °F		ISO 178
 50.0 MPa
@Thickness 2.00 mm,
Temperature 200 °C		7250 psi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 178
 55.0 MPa
@Thickness 1.00 mm,
Temperature 200 °C		7980 psi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 178
 70.0 MPa
@Thickness 4.00 mm,
Temperature 150 °C		10200 psi
@Thickness 0.157 in,
Temperature 302 °F		ISO 178
 80.0 MPa
@Thickness 4.00 mm,
Temperature 120 °C		11600 psi
@Thickness 0.157 in,
Temperature 248 °F		ISO 178
 80.0 MPa
@Thickness 2.00 mm,
Temperature 150 °C		11600 psi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 178
 90.0 MPa
@Thickness 1.00 mm,
Temperature 150 °C		13100 psi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 178
 90.0 MPa
@Thickness 2.00 mm,
Temperature 120 °C		13100 psi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 178
 100 MPa
@Thickness 1.00 mm,
Temperature 120 °C		14500 psi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 178
 180 MPa
@Thickness 4.00 mm,
Temperature 23.0 °C		26100 psi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 178
 210 MPa
@Thickness 2.00 mm,
Temperature 23.0 °C		30500 psi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 178
 230 MPa
@Thickness 1.00 mm,
Temperature 23.0 °C		33400 psi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 178
 240 MPa
@Thickness 4.00 mm,
Temperature -30.0 °C		34800 psi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 178
 250 MPa
@Thickness 4.00 mm,
Temperature -40.0 °C		36300 psi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 178
 255 MPa
@Thickness 2.00 mm,
Temperature -30.0 °C		37000 psi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 178
 270 MPa
@Thickness 2.00 mm,
Temperature -40.0 °C		39200 psi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 178
 280 MPa
@Thickness 1.00 mm,
Temperature -30.0 °C		40600 psi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 178
 300 MPa
@Thickness 1.00 mm,
Temperature -40.0 °C		43500 psi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 178
Flexural Modulus  5.00 GPa
@Thickness 4.00 mm,
Temperature 250 °C		725 ksi
@Thickness 0.157 in,
Temperature 482 °F		ISO 178
 8.00 GPa
@Thickness 2.00 mm,
Temperature 250 °C		1160 ksi
@Thickness 0.0787 in,
Temperature 482 °F		ISO 178
 9.00 GPa
@Thickness 1.00 mm,
Temperature 250 °C		1310 ksi
@Thickness 0.0394 in,
Temperature 482 °F		ISO 178
 9.00 GPa
@Thickness 4.00 mm,
Temperature 200 °C		1310 ksi
@Thickness 0.157 in,
Temperature 392 °F		ISO 178
 10.0 GPa
@Thickness 2.00 mm,
Temperature 200 °C		1450 ksi
@Thickness 0.0787 in,
Temperature 392 °F		ISO 178
 12.0 GPa
@Thickness 1.00 mm,
Temperature 200 °C		1740 ksi
@Thickness 0.0394 in,
Temperature 392 °F		ISO 178
 12.5 GPa
@Thickness 4.00 mm,
Temperature 150 °C		1810 ksi
@Thickness 0.157 in,
Temperature 302 °F		ISO 178
 13.0 GPa
@Thickness 4.00 mm,
Temperature 120 °C		1890 ksi
@Thickness 0.157 in,
Temperature 248 °F		ISO 178
 14.0 GPa
@Thickness 2.00 mm,
Temperature 150 °C		2030 ksi
@Thickness 0.0787 in,
Temperature 302 °F		ISO 178
 15.0 GPa
@Thickness 2.00 mm,
Temperature 120 °C		2180 ksi
@Thickness 0.0787 in,
Temperature 248 °F		ISO 178
 15.0 GPa
@Thickness 1.00 mm,
Temperature 150 °C		2180 ksi
@Thickness 0.0394 in,
Temperature 302 °F		ISO 178
 17.5 GPa
@Thickness 4.00 mm,
Temperature 23.0 °C		2540 ksi
@Thickness 0.157 in,
Temperature 73.4 °F		ISO 178
 18.0 GPa
@Thickness 1.00 mm,
Temperature 120 °C		2610 ksi
@Thickness 0.0394 in,
Temperature 248 °F		ISO 178
 20.0 GPa
@Thickness 4.00 mm,
Temperature -30.0 °C		2900 ksi
@Thickness 0.157 in,
Temperature -22.0 °F		ISO 178
 20.5 GPa
@Thickness 2.00 mm,
Temperature 23.0 °C		2970 ksi
@Thickness 0.0787 in,
Temperature 73.4 °F		ISO 178
 21.0 GPa
@Thickness 4.00 mm,
Temperature -40.0 °C		3050 ksi
@Thickness 0.157 in,
Temperature -40.0 °F		ISO 178
 21.5 GPa
@Thickness 2.00 mm,
Temperature -30.0 °C		3120 ksi
@Thickness 0.0787 in,
Temperature -22.0 °F		ISO 178
 22.5 GPa
@Thickness 2.00 mm,
Temperature -40.0 °C		3260 ksi
@Thickness 0.0787 in,
Temperature -40.0 °F		ISO 178
 24.0 GPa
@Thickness 1.00 mm,
Temperature 23.0 °C		3480 ksi
@Thickness 0.0394 in,
Temperature 73.4 °F		ISO 178
 25.0 GPa
@Thickness 1.00 mm,
Temperature -30.0 °C		3630 ksi
@Thickness 0.0394 in,
Temperature -22.0 °F		ISO 178
 25.5 GPa
@Thickness 1.00 mm,
Temperature -40.0 °C		3700 ksi
@Thickness 0.0394 in,
Temperature -40.0 °F		ISO 178
Charpy Impact Unnotched  1.30 J/cm²
@Temperature -30.0 °C		6.19 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 1.80 J/cm²
@Temperature 23.0 °C		8.57 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm²
@Temperature -30.0 °C		4.76 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.00 J/cm²
@Temperature 23.0 °C		4.76 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Melting Point 352 °C666 °F10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 295 °C563 °FISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 365 °C689 °FOptimum
 360 - 370 °C680 - 698 °F
Mold Temperature 80.0 °C176 °FOptimum
 40.0 - 150 °C104 - 302 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hourDehumidified Dryer
Moisture Content <= 0.010 %<= 0.010 %
 
Descriptive Properties
ColorBlack
Drying RecommendedYes
FillerGlass Reinforced
FormsPellets
GenericLCP
Part Marking Code>LCP-GF45<ISO 11469
Polymer FamilyLCP
Polymer TypeLCP
Processing MethodInjection Molding
Product CategoryFood Contact Resins
 Glass Reinforced Resins
Region AvailableAmericas
 Asia/Pacific
 Europe
Resin IdentificationLCP-GF45ISO 1043

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31779.html

免责声明: 本文 Celanese Zenite® FG7145L BK011 LCP 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4