- 密度 [g/cm3]: 1.63
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 10.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 40.0 | 40.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.20 % | 2.20 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 10.9 GPa | 1580 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 | ||
| Flexural Modulus | 10.9 GPa | 1580 ksi | ISO 178 | ||
| Compressive Strength | 59.0 MPa | 8560 psi | 1% strain; ISO 604 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | ISO 180/1U | ||
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.90 @Frequency 1.00e+6 Hz | 3.90 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 49.0 kV/mm | 1240 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.340 @Frequency 1.00e+6 Hz | 0.340 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 11.0 µm/m-°C | 6.11 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 159 °C | 318 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 190 °C | 374 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 320 - 330 °C | 608 - 626 °F | |||
| Zone 3 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 4 | 330 - 340 °C | 626 - 644 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Screw Speed | 100 rpm @Diameter 25.0 mm | 100 rpm @Diameter 0.984 in | |||
| 120 rpm @Diameter 40.0 mm | 120 rpm @Diameter 1.57 in | ||||
| 150 rpm @Diameter 55.0 mm | 150 rpm @Diameter 2.17 in | ||||
| 200 rpm @Diameter 75.0 mm | 200 rpm @Diameter 2.95 in | ||||
| Descriptive Properties | |||||
| Injection speed | high | ||||