- 密度 [g/cm3]: 1.71
- 弯曲模量 [MPa]: 13.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 131 MPa | 19000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.66 % | 1.66 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 198 MPa | 28700 psi | ISO 178 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 2.70 J/cm² | 12.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.66 J/cm² | 7.90 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.18 @Frequency 2.05e+9 Hz | 4.18 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 |
| Dissipation Factor | 0.00400 @Frequency 2.05e+9 Hz | 0.00400 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C | 26.7 µin/in-°F | ISO 11359-2 |
| Melting Point | 318 °C | 604 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL94 |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 320 - 330 °C | 608 - 626 °F | |
| Zone 2 | 335 - 345 °C | 635 - 653 °F | |
| Zone 3 | 335 - 345 °C | 635 - 653 °F | |
| Zone 4 | 335 - 345 °C | 635 - 653 °F | |
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |
| Melt Temperature | 325 - 345 °C | 617 - 653 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi | |