Celanese Vectra® L130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced

Celanese Vectra® L130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced 物性表: Celanese Vectra® L130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced物性表及特性介绍,Celanese Vectra® L130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced注塑参数详情,如需Celanese Vectra® L130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.61
  • 吸水率 [%]: 0.04
  • 缺口冲击强度: 23.0
  • 弯曲强度 [MPa]: 155.0
  • 弯曲模量 [MPa]: 16.0
 
Physical PropertiesMetricEnglishComments
Density 1.61 g/cc0.0582 lb/in³ISO 1183
Water Absorption 0.040 %0.040 %Immersion to equilibrium; ISO 62
Moisture Absorption at Equilibrium 0.040 %0.040 %ISO 62
Linear Mold Shrinkage 0.0010 cm/cm0.0010 in/in
Linear Mold Shrinkage, Transverse 0.0020 cm/cm0.0020 in/in
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 155 MPa22500 psiISO 527
Elongation at Break 1.6 %1.6 %IEC 527
Tensile Modulus 15.0 GPa2180 ksiISO 527
Flexural Strength 230 MPa33400 psiISO 178
Flexural Modulus 16.0 GPa2320 ksiISO 178
Compressive Strength 100 MPa14500 psi1% Deflection, ISO 604
Compressive Modulus 14.0 GPa2030 ksiISO 604
Izod Impact, Notched (ISO) 23.0 kJ/m²10.9 ft-lb/in²ISO 180/1A
Charpy Impact, Notched 4.30 J/cm²20.5 ft-lb/in²ISO 179
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 1.00e+12 ohm-cm1.00e+12 ohm-cmIEC 93
Surface Resistance 1.00e+17 ohm1.00e+17 ohmIEC 93
Dielectric Constant  3.3
@Frequency 1e+7 Hz
3.3
@Frequency 1e+7 Hz
 3.8
@Frequency 1000 Hz
3.8
@Frequency 1000 Hz
IEC 250
Dissipation Factor  0.020
@Frequency 1000 Hz
0.020
@Frequency 1000 Hz
IEC 250
 0.020
@Frequency 1e+7 Hz
0.020
@Frequency 1e+7 Hz
Arc Resistance 130 sec130 sec
Comparative Tracking Index 175 V175 VIEC 112
 
Thermal PropertiesMetricEnglishComments
CTE, linear  5.00 µm/m-°C
@Temperature -50.0 - 200 °C
2.78 µin/in-°F
@Temperature -58.0 - 392 °F
Flow Direction
 5.00 µm/m-°C
@Temperature -58.0 - 390 °C
2.78 µin/in-°F
@Temperature -72.4 - 734 °F
Flow Direction
CTE, linear, Transverse to Flow  65.0 µm/m-°C
@Temperature -50.0 - 200 °C
36.1 µin/in-°F
@Temperature -58.0 - 392 °F
 65.0 µm/m-°C
@Temperature -50.0 - 200 °C
36.1 µin/in-°F
@Temperature -58.0 - 392 °F
Melting Point 302 °C576 °FISO 3146
Maximum Service Temperature, Air 130 °C266 °FGeneric Rating for Vectra LCP
Deflection Temperature at 1.8 MPa (264 psi) 235 °C455 °FISO 75/A
UL RTI, Electrical 130 °C266 °FGeneric Rating for Vectra LCP
UL RTI, Mechanical with Impact 130 °C266 °FGeneric Rating for Vectra LCP
Flammability, UL94 V-0V-0
Oxygen Index 45 %45 %ISO 4589

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31881.html

免责声明: 本文 Celanese Vectra® L130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4