Celanese Vectra® A540 Liquid Crystal Polymer (LCP), 40% Mineral Filled

Celanese Vectra® A540 Liquid Crystal Polymer (LCP), 40% Mineral Filled 物性表: Celanese Vectra® A540 Liquid Crystal Polymer (LCP), 40% Mineral Filled物性表及特性介绍,Celanese Vectra® A540 Liquid Crystal Polymer (LCP), 40% Mineral Filled注塑参数详情,如需Celanese Vectra® A540 Liquid Crystal Polymer (LCP), 40% Mineral Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.76
  • 吸水率 [%]: 0.02
  • 缺口冲击强度: 20.0
  • 弯曲强度 [MPa]: 155.0
  • 弯曲模量 [MPa]: 16.0
 
Physical PropertiesMetricEnglishComments
Density 1.76 g/cc0.0636 lb/in³ISO 1183
Water Absorption 0.020 %0.020 %Immersion to equilibrium; ISO 62
Moisture Absorption at Equilibrium 0.020 %0.020 %ISO 62
Linear Mold Shrinkage 0.0020 cm/cm0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0040 cm/cm0.0040 in/in
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 6363ISO 2039-2
Tensile Strength, Ultimate 155 MPa22500 psiISO 527
Elongation at Break 3.9 %3.9 %IEC 527
Tensile Modulus 19.0 GPa2760 ksiISO 527
Flexural Strength 195 MPa28300 psiISO 178
Flexural Modulus 16.0 GPa2320 ksiISO 178
Compressive Strength 78.0 MPa11300 psi1% Deflection, ISO 604
Compressive Modulus 12.0 GPa1740 ksiISO 604
Izod Impact, Notched (ISO) 20.0 kJ/m²9.52 ft-lb/in²ISO 180/1A
Charpy Impact, Notched 4.00 J/cm²19.0 ft-lb/in²ISO 179
Tensile Impact Strength 40.0 kJ/m²19.0 ft-lb/in²Notched; ASTM D1822
Coefficient of Friction, Dynamic 0.120.12vs. steel; ASTM D1984
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 1.00e+12 ohm-cm1.00e+12 ohm-cmIEC 93
Surface Resistance 1.00e+16 ohm1.00e+16 ohmIEC 93
Dielectric Constant  3.7
@Frequency 1e+7 Hz
3.7
@Frequency 1e+7 Hz
 4.2
@Frequency 1000 Hz
4.2
@Frequency 1000 Hz
IEC 250
Dissipation Factor  0.0080
@Frequency 1e+7 Hz
0.0080
@Frequency 1e+7 Hz
 0.020
@Frequency 1000 Hz
0.020
@Frequency 1000 Hz
IEC 250
Arc Resistance 180 sec180 sec
Comparative Tracking Index 200 V200 VIEC 112
 
Thermal PropertiesMetricEnglishComments
CTE, linear  0.000 µm/m-°C
@Temperature -50.0 - 200 °C
0.000 µin/in-°F
@Temperature -58.0 - 392 °F
Flow Direction
 0.000 µm/m-°C
@Temperature -58.0 - 390 °C
0.000 µin/in-°F
@Temperature -72.4 - 734 °F
Flow Direction
CTE, linear, Transverse to Flow  50.0 µm/m-°C
@Temperature -50.0 - 200 °C
27.8 µin/in-°F
@Temperature -58.0 - 392 °F
 50.0 µm/m-°C
@Temperature -50.0 - 200 °C
27.8 µin/in-°F
@Temperature -58.0 - 392 °F
Melting Point 280 °C536 °FISO 3146
Maximum Service Temperature, Air 130 °C266 °FGeneric Rating for Vectra LCP
Deflection Temperature at 1.8 MPa (264 psi) 200 °C392 °FISO 75/A
UL RTI, Electrical 130 °C266 °FGeneric Rating for Vectra LCP
UL RTI, Mechanical with Impact 130 °C266 °FGeneric Rating for Vectra LCP
Flammability, UL94 V-0V-0

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31891.html

免责声明: 本文 Celanese Vectra® A540 Liquid Crystal Polymer (LCP), 40% Mineral Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4