- 密度 [g/cm3]: 1.85
- 缺口冲击强度: 2.0
- 弯曲模量 [MPa]: 10.8
- 热变形温度 [℃]: 246.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.4 GPa | 1650 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 133 MPa | 19300 psi | ISO 178 |
| Flexural Modulus | 10.8 GPa | 1570 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz | 3.7 @Frequency 1e+6 Hz | IEC 60250 |
| 4.2 @Frequency 100 Hz | 4.2 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0060 @Frequency 100 Hz | 0.0060 @Frequency 100 Hz | IEC 60250 |
| 0.014 @Frequency 1e+6 Hz | 0.014 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 23.0 µm/m-°C @Temperature 20.0 °C | 12.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 325 °C | 617 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 119 °C | 246 °F | ISO 75-1, -2 |
| Vicat Softening Point | 180 °C | 356 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | thickness h |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 209 - 300 °C | 408 - 572 °F | |
| Middle Barrel Temperature | 310 - 320 °C | 590 - 608 °F | |
| Front Barrel Temperature | 320 - 330 °C | 608 - 626 °F | |
| Nozzle Temperature | 300 - 330 °C | 572 - 626 °F | |
| Melt Temperature | 320 - 330 °C | 608 - 626 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |