- 密度 [g/cm3]: 1.35
- 成型收缩率 [%]: 0.001
- 缺口冲击强度: 1.17
- 拉伸强度 [MPa]: 121.0
- 弯曲模量 [MPa]: 11.72
- 热变形温度 [℃]: 263.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Filler Content | 40 % | 40 % | Glass |
| Moisture Absorption | 0.0100 % | 0.0100 % | 24 hours, 50% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 0.0625 mm | 0.0010 - 0.0030 in/in @Thickness 0.00246 in | ASTM D966 |
| 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm | 0.0020 - 0.0050 in/in @Thickness 0.125 in | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0090 cm/cm @Thickness 0.0625 mm | 0.0040 - 0.0090 in/in @Thickness 0.00246 in | ASTM D966 |
| 0.0040 - 0.010 cm/cm @Thickness 3.17 mm | 0.0040 - 0.010 in/in @Thickness 0.125 in | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 121 MPa | 17500 psi | ASTM D638 |
| Tensile Strength, Yield | 121 MPa | 17500 psi | ASTM D638 |
| Elongation at Break | 1.2 % | 1.2 % | ASTM D638 |
| Tensile Modulus | 11.2 GPa | 1620 ksi | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 11.72 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Temperature 23.0 °C | 2.19 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| 1.17 J/cm @Temperature -17.8 °C | 2.19 ft-lb/in @Temperature -0.0400 °F | ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.30e+12 ohm-cm | 1.30e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 | 3.1 | ASTM D150 |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 | 0.0010 | ASTM D150 |
| Comparative Tracking Index | 380 V | 380 V | ASTM D3638 |
| Hot Wire Ignition, HWI | 107 sec @Thickness 3.00 mm | 107 sec @Thickness 0.118 in | No Drip |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 17.0 µm/m-°C @Thickness 3.20 mm, Temperature 100 °C | 9.44 µin/in-°F @Thickness 0.126 in, Temperature 212 °F | Unannealed; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 263 °C @Thickness 3.20 mm | 505 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C @Thickness 3.20 mm | 460 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Vicat Softening Point | 263 °C @Thickness 3.20 mm | 505 °F @Thickness 0.126 in | unannealed; ASTM D1525 |
| Flammability, UL94 | HB | HB | |