- 熔体流动速率 [g/10min]: 13.8
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D792 | ||
| Melt Flow | 13.8 g/10 min @Load 2.16 kg, Temperature 125 °C | 13.8 g/10 min @Load 4.76 lb, Temperature 257 °F | ASTM D1238 | ||
| Melt Index of Compound | 300 g/10 min @Load 2.16 kg, Temperature 125 °C | 300 g/10 min @Load 4.76 lb, Temperature 257 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 50 | 50 | Compression molded; ASTM D2240 | ||
| Tensile Strength at Break | 9.65 MPa | 1400 psi | Compression molded; ASTM D638 | ||
| Elongation at Break | 390 % | 390 % | Compression molded; ASTM D638 | ||
| Tensile Modulus | 0.0331 GPa | 4.80 ksi | 2% Secant; Compression molded; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 77.2 °C | 171 °F | Dow Method (DSC) | ||
| Vicat Softening Point | 42.2 °C | 108 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Comonomer content, % | 20.5 | measured by direct titration | |||