- 熔体流动速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.94
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.108
- 拉伸强度 [MPa]: 32.0
- 断裂伸长率 [%]: 9.22
- 弯曲强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 1.80
- 热变形温度 [℃]: 75.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 - 1.17 g/cc | 0.0340 - 0.0423 lb/in³ | Average value: 1.03 g/cc Grade Count:41 |
| Water Absorption | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:17 |
| Water Absorption at Saturation | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:15 |
| Moisture Vapor Transmission | 0.0900 - 0.110 cc-mm/m²-24hr-atm | 0.229 - 0.279 cc-mil/100 in²-24hr-atm | Average value: 0.0922 cc-mm/m²-24hr-atm Grade Count:9 |
| Water Vapor Transmission | 0.0000250 - 0.250 g/m²/day | 0.00000161 - 0.0161 g/100 in²/day | Average value: 0.111 g/m²/day Grade Count:8 |
| 0.000100 - 0.000800 g/m²/day @Temperature 38.0 - 38.0 °C | 0.00000644 - 0.0000515 g/100 in²/day @Temperature 100 - 100 °F | Average value: 0.000343 g/m²/day Grade Count:3 | |
| Oxygen Transmission | 0.0400 - 28.0 cc-mm/m²-24hr-atm | 0.102 - 71.1 cc-mil/100 in²-24hr-atm | Average value: 17.7 cc-mm/m²-24hr-atm Grade Count:3 |
| Thickness | 70.0 - 127 microns | 2.76 - 5.00 mil | Average value: 82.4 microns Grade Count:7 |
| Linear Mold Shrinkage | 0.00100 - 0.00700 cm/cm | 0.00100 - 0.00700 in/in | Average value: 0.00540 cm/cm Grade Count:10 |
| Melt Flow | 0.100 - 60.0 g/10 min | 0.100 - 60.0 g/10 min | Average value: 15.7 g/10 min Grade Count:39 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 32.0 - 75.8 MPa | 4640 - 11000 psi | Average value: 57.3 MPa Grade Count:15 |
| Tensile Strength, Yield | 32.0 - 72.0 MPa | 4640 - 10400 psi | Average value: 57.1 MPa Grade Count:20 |
| Film Elongation at Break, MD | 1.40 - 800 % | 1.40 - 800 % | Average value: 200 % Grade Count:7 |
| Film Elongation at Break, TD | 1.10 - 790 % | 1.10 - 790 % | Average value: 190 % Grade Count:7 |
| Elongation at Break | 0.500 - 140 % | 0.500 - 140 % | Average value: 24.1 % Grade Count:21 |
| Elongation at Yield | 1.70 - 40.0 % | 1.70 - 40.0 % | Average value: 7.40 % Grade Count:14 |
| Modulus of Elasticity | 0.0340 - 16.0 GPa | 4.93 - 2330 ksi | Average value: 2.92 GPa Grade Count:34 |
| Flexural Yield Strength | 9.22 - 158 MPa | 1340 - 22900 psi | Average value: 95.6 MPa Grade Count:17 |
| Flexural Modulus | 1.80 - 16.7 GPa | 261 - 2420 ksi | Average value: 4.31 GPa Grade Count:17 |
| 1.70 - 2.70 GPa @Temperature 40.0 - 130 °C | 247 - 392 ksi @Temperature 104 - 266 °F | Average value: 2.13 GPa Grade Count:2 | |
| Izod Impact, Notched | 0.108 - 0.800 J/cm | 0.202 - 1.50 ft-lb/in | Average value: 0.345 J/cm Grade Count:18 |
| Izod Impact, Unnotched (ISO) | 10.0 - 33.0 kJ/m² | 4.76 - 15.7 ft-lb/in² | Average value: 17.2 kJ/m² Grade Count:6 |
| Charpy Impact Unnotched | 1.30 - 2.50 J/cm² | 6.19 - 11.9 ft-lb/in² | Average value: 1.65 J/cm² Grade Count:15 |
| Charpy Impact, Notched | 0.160 - 0.260 J/cm² | 0.761 - 1.24 ft-lb/in² | Average value: 0.196 J/cm² Grade Count:15 |
| Elmendorf Tear Strength MD | 9.00 - 2720 g | 9.00 - 2720 g | Average value: 716 g Grade Count:5 |
| Elmendorf Tear Strength TD | 9.00 - 3170 g | 9.00 - 3170 g | Average value: 814 g Grade Count:5 |
| Dart drop Test | 36.0 g | 0.0794 lb | Average value: 36.0 g Grade Count:4 |
| Film Tensile Strength at Break, MD | 25.0 - 57.0 MPa | 3630 - 8270 psi | Average value: 47.0 MPa Grade Count:6 |
| Film Tensile Strength at Break, TD | 22.0 - 55.0 MPa | 3190 - 7980 psi | Average value: 41.2 MPa Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+17 ohm-cm | 1.00e+12 - 1.00e+17 ohm-cm | Average value: 1.57e+16 ohm-cm Grade Count:14 |
| Surface Resistance | 10.0 - 1.00e+14 ohm | 10.0 - 1.00e+14 ohm | Average value: 3.33e+13 ohm Grade Count:3 |
| Dielectric Constant | 2.20 - 2.35 | 2.20 - 2.35 | Average value: 2.29 Grade Count:19 |
| Dielectric Strength | 40.0 - 157 kV/mm | 1020 - 4000 kV/in | Average value: 81.5 kV/mm Grade Count:5 |
| Dissipation Factor | 0.0000700 - 0.000260 | 0.0000700 - 0.000260 | Average value: 0.000131 Grade Count:12 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 2.80 - 70.0 µm/m-°C | 1.56 - 38.9 µin/in-°F | Average value: 49.4 µm/m-°C Grade Count:7 |
| Melting Point | 80.0 - 155 °C | 176 - 311 °F | Average value: 120 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 - 170 °C | 167 - 338 °F | Average value: 122 °C Grade Count:17 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 - 151 °C | 140 - 304 °F | Average value: 110 °C Grade Count:21 |
| Vicat Softening Point | 64.0 - 178 °C | 147 - 352 °F | Average value: 117 °C Grade Count:9 |
| Glass Transition Temp, Tg | 33.0 - 180 °C | 91.4 - 356 °F | Average value: 118 °C Grade Count:40 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:13 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.51 - 1.54 | 1.51 - 1.54 | Average value: 1.53 Grade Count:29 |
| Haze | 1.00 - 8.50 % | 1.00 - 8.50 % | Average value: 2.38 % Grade Count:13 |
| Gloss | 94.0 - 116 % | 94.0 - 116 % | Average value: 101 % Grade Count:6 |
| Transmission, Visible | 90.0 - 94.0 % | 90.0 - 94.0 % | Average value: 91.2 % Grade Count:32 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 60.0 - 110 °C | 140 - 230 °F | Average value: 87.5 °C Grade Count:8 |
| Nozzle Temperature | 220 - 320 °C | 428 - 608 °F | Average value: 265 °C Grade Count:10 |
| Melt Temperature | 84.0 - 320 °C | 183 - 608 °F | Average value: 249 °C Grade Count:11 |
| Mold Temperature | 40.0 - 160 °C | 104 - 320 °F | Average value: 100 °C Grade Count:10 |
| Injection Velocity | 50.0 - 150 mm/sec | 1.97 - 5.91 in/sec | Average value: 100 mm/sec Grade Count:7 |
| Injection Pressure | 50.0 - 110 MPa | 7250 - 16000 psi | Average value: 80.0 MPa Grade Count:7 |
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | Average value: 45.0 MPa Grade Count:7 |
| Back Pressure | 15.0 MPa | 2180 psi | Average value: 15.0 MPa Grade Count:7 |
| Screw Speed | 50.0 - 200 rpm | 50.0 - 200 rpm | Average value: 125 rpm Grade Count:7 |