- 缺口冲击强度: 0.35
- 拉伸强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 2.50
- 透光率 [%]: 91.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ASTM D792 |
| Moisture Vapor Transmission | 0.0900 cc-mm/m²-24hr-atm | 0.229 cc-mil/100 in²-24hr-atm | 1 atm; ASTM D1249 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MCI Method |
| Melt Index of Compound | 30 g/10 min @Load 2.16 kg, Temperature 260 °C | 30 g/10 min @Load 4.76 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | TMA; MCI Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | MCI Method |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.54 | 1.54 | ASTM D542 |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D1003 |