Mitsui APEL™ APL6015T Cyclo Olefin Copolymer (COC)

Mitsui APEL™ APL6015T Cyclo Olefin Copolymer (COC) 物性表: Mitsui APEL™ APL6015T Cyclo Olefin Copolymer (COC)物性表及特性介绍,Mitsui APEL™ APL6015T Cyclo Olefin Copolymer (COC)注塑参数详情,如需Mitsui APEL™ APL6015T Cyclo Olefin Copolymer (COC)下载, 可到相关下载区下载
  • 缺口冲击强度: 0.25
  • 拉伸强度 [MPa]: 60.0
  • 弯曲模量 [MPa]: 3.20
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.04 g/cc1.04 g/ccASTM D792
Moisture Vapor Transmission 0.0900 cc-mm/m²-24hr-atm0.229 cc-mil/100 in²-24hr-atm1 atm; ASTM D1249
Linear Mold Shrinkage 0.0060 cm/cm0.0060 in/inMCI Method
Melt Index of Compound 10 g/10 min
@Load 2.16 kg,
Temperature 260 °C
10 g/10 min
@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 60.0 MPa8700 psiASTM D638
Elongation at Break 3.0 %3.0 %ASTM D638
Flexural Strength 110 MPa16000 psiASTM D790
Flexural Modulus 3.20 GPa464 ksiASTM D790
Izod Impact, Notched 0.250 J/cm0.468 ft-lb/inASTM D256
Izod Impact, Unnotched (ISO) 10.0 kJ/m²4.76 ft-lb/in²ASTM D256
 
Thermal PropertiesMetricEnglishComments
Melting Point 155 °C311 °FTMA; MCI Method
Deflection Temperature at 1.8 MPa (264 psi) 135 °C275 °FASTM D648
Glass Transition Temp, Tg 145 °C293 °FMCI Method
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.541.54ASTM D542
Haze 4.0 %4.0 %ASTM D1003
Transmission, Visible 90 %90 %ASTM D1003

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-32152.html

免责声明: 本文 Mitsui APEL™ APL6015T Cyclo Olefin Copolymer (COC) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4