- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.8
- 缺口冲击强度: 8.0
- 拉伸强度 [MPa]: 4.62
- 断裂伸长率 [%]: 110
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 6.41
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 2.25 g/cc | 0.0415 - 0.0813 lb/in³ | Average value: 1.47 g/cc Grade Count:33 |
| Volatiles | 1.00 - 6.00 % | 1.00 - 6.00 % | Average value: 2.43 % Grade Count:7 |
| Water Absorption | 0.800 - 3.90 % | 0.800 - 3.90 % | Average value: 2.87 % Grade Count:3 |
| Viscosity | 25000 - 450000 cP | 25000 - 450000 cP | Average value: 242000 cP Grade Count:6 |
| 5000 - 35000 cP @Temperature 60.0 - 60.0 °C | 5000 - 35000 cP @Temperature 140 - 140 °F | Average value: 20000 cP Grade Count:3 | |
| Linear Mold Shrinkage | 0.000 cm/cm | 0.000 in/in | Average value: 0.000 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 60.0 - 65.0 | 60.0 - 65.0 | Average value: 63.3 Grade Count:3 |
| Tensile Strength, Ultimate | 50.0 - 2100 MPa | 7250 - 305000 psi | Average value: 760 MPa Grade Count:22 |
| Tensile Strength, Yield | 4.62 - 2650 MPa | 670 - 384000 psi | Average value: 1080 MPa Grade Count:40 |
| 2.965 - 2137 MPa @Temperature -59.0 - 177 °C | 430.0 - 309900 psi @Temperature -74.2 - 351 °F | Average value: 945 MPa Grade Count:19 | |
| Elongation at Break | 0.500 - 11.0 % | 0.500 - 11.0 % | Average value: 1.94 % Grade Count:3 |
| Modulus of Elasticity | 6.60 - 520 GPa | 957 - 75400 ksi | Average value: 105 GPa Grade Count:59 |
| 5.30 - 140 GPa @Temperature -55.0 - 177 °C | 769 - 20300 ksi @Temperature -67.0 - 351 °F | Average value: 86.9 GPa Grade Count:18 | |
| Flexural Yield Strength | 110 - 2000 MPa | 16000 - 290000 psi | Average value: 915 MPa Grade Count:32 |
| 515 - 1448 MPa @Temperature 71.0 - 90.0 °C | 74700 - 210000 psi @Temperature 160 - 194 °F | Average value: 967 MPa Grade Count:9 | |
| Flexural Modulus | 6.41 - 199 GPa | 930 - 28900 ksi | Average value: 75.9 GPa Grade Count:30 |
| 37.0 - 191 GPa @Temperature 71.0 - 90.0 °C | 5370 - 27700 ksi @Temperature 160 - 194 °F | Average value: 101 GPa Grade Count:8 | |
| Compressive Yield Strength | 50.0 - 1720 MPa | 7250 - 249000 psi | Average value: 829 MPa Grade Count:54 |
| 350 - 1786 MPa @Temperature -59.0 - 150 °C | 50800 - 259000 psi @Temperature -74.2 - 302 °F | Average value: 888 MPa Grade Count:26 | |
| Compressive Modulus | 8.20 - 138 GPa | 1190 - 20000 ksi | Average value: 72.5 GPa Grade Count:25 |
| 36.0 - 119.3 GPa @Temperature -59.0 - 130 °C | 5220 - 17300 ksi @Temperature -74.2 - 266 °F | Average value: 84.5 GPa Grade Count:11 | |
| Shear Modulus | 3.00 - 5.00 GPa | 435 - 725 ksi | Average value: 3.83 GPa Grade Count:3 |
| 2.00 - 2.40 GPa @Temperature 130 - 130 °C | 290 - 348 ksi @Temperature 266 - 266 °F | Average value: 2.20 GPa Grade Count:2 | |
| Shear Strength | 30.0 - 120 MPa | 4350 - 17400 psi | Average value: 74.6 MPa Grade Count:44 |
| 26.2 - 124 MPa @Temperature -55.0 - 177 °C | 3800 - 18000 psi @Temperature -67.0 - 351 °F | Average value: 57.4 MPa Grade Count:22 | |
| Izod Impact, Notched | 8.00 - 15.0 J/cm | 15.0 - 28.1 ft-lb/in | Average value: 10.4 J/cm Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100 - 1.30e+13 ohm-cm | 100 - 1.30e+13 ohm-cm | Average value: 1.00e+12 ohm-cm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | -0.700 - 29.7 µm/m-°C | -0.389 - 16.5 µin/in-°F | Average value: 9.09 µm/m-°C Grade Count:10 |
| CTE, linear, Transverse to Flow | 2.10 - 225 µm/m-°C | 1.17 - 125 µin/in-°F | Average value: 82.5 µm/m-°C Grade Count:3 |
| Specific Heat Capacity | 1.00 - 1.20 J/g-°C | 0.239 - 0.287 BTU/lb-°F | Average value: 1.13 J/g-°C Grade Count:3 |
| Thermal Conductivity | 0.220 - 400 W/m-K | 1.53 - 2780 BTU-in/hr-ft²-°F | Average value: 78.8 W/m-K Grade Count:12 |
| Maximum Service Temperature, Air | 120 - 300 °C | 248 - 572 °F | Average value: 176 °C Grade Count:9 |
| Glass Transition Temp, Tg | 76.1 - 170 °C | 169 - 338 °F | Average value: 107 °C Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 127 - 166 °C | 260 - 330 °F | Average value: 143 °C Grade Count:7 |
| Cure Time | 5.00 - 10.0 min | 0.0833 - 0.167 hour | Average value: 7.50 min Grade Count:3 |
| 5.00 - 10.0 min @Temperature 138 - 138 °C | 0.0833 - 0.167 hour @Temperature 280 - 280 °F | Average value: 7.50 min Grade Count:1 | |
| Shelf Life | 6.00 - 14.0 Month @Temperature -18.0 - -12.2 °C | 6.00 - 14.0 Month @Temperature -0.400 - 10.0 °F | Average value: 11.5 Month Grade Count:21 |