- 密度 [g/cm3]: 1.09
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.09 g/cc | 0.0394 lb/in³ | Part B | ||
1.14 g/cc | 0.0411 lb/in³ | Part A | |||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 55.2 MPa | 8000 psi | |||
Elongation at Break | 27 % | 27 % | |||
Tensile Modulus | 5.45 GPa | 790 ksi | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |||
Dielectric Constant | 2.9 @Frequency 60.0 Hz, Temperature 23.0 °C | 2.9 @Frequency 60.0 Hz, Temperature 73.4 °F | |||
3.2 @Frequency 60.0 Hz, Temperature 100 °C | 3.2 @Frequency 60.0 Hz, Temperature 212 °F | ||||
3.3 @Frequency 60.0 Hz, Temperature 150 °C | 3.3 @Frequency 60.0 Hz, Temperature 302 °F | ||||
Dissipation Factor | 0.010 @Frequency 60.0 Hz, Temperature 23.0 °C | 0.010 @Frequency 60.0 Hz, Temperature 73.4 °F | |||
0.031 @Frequency 60.0 Hz, Temperature 100 °C | 0.031 @Frequency 60.0 Hz, Temperature 212 °F | ||||
0.080 @Frequency 60.0 Hz, Temperature 150 °C | 0.080 @Frequency 60.0 Hz, Temperature 302 °F | ||||
Arc Resistance | >= 150 sec | >= 150 sec | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 100 °C | 212 °F | Deflection Temp at unknown load | ||
Processing Properties | Metric | English | Comments | ||
Cure Time | 120 - 180 min @Temperature 100 °C | 2.00 - 3.00 hour @Temperature 212 °F | |||
60.0 - 240 min @Temperature 120 - 160 °C | 1.00 - 4.00 hour @Temperature 248 - 320 °F | optional | |||
Pot Life | 30 min @Temperature 80.0 °C | 30 min @Temperature 176 °F | |||
>= 480 min @Temperature 25.0 °C | >= 480 min @Temperature 77.0 °F | ||||
Descriptive Properties | |||||
Arc-Track Free (min) | > 2000 | 2.5 KV | |||
Color | Clear | ||||
Parts by Weight (pbw) | 100 | Part A | |||
65 | Part B | ||||
Thermal Shock Resistance | Scale 0 (poor) to 10 (excellent) |