- 吸水率 [%]: 2.5
- 弯曲强度 [MPa]: 43.33
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 2.5 % @Time 7200 sec | 2.5 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | ||
| Viscosity | 2000 cP | 2000 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 75 @Temperature 75.0 °C | 75 @Temperature 167 °F | cured 2 hrs. @ 93°C | ||
| 83 @Temperature 25.0 °C | 83 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | |||
| 87 @Temperature 0.000 °C | 87 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 90 @Temperature -60.0 °C | 90 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| Tensile Strength, Ultimate | 43.33 MPa | 6285 psi | cured 2 hours @ 93°C | ||
| 58.16 MPa | 8435 psi | cured 8 hours @ 93°C | |||
| Elongation at Break | 11 % | 11 % | cured 8 hours @ 93°C | ||
| 13 % | 13 % | cured 2 hours @ 93°C | |||
| Shear Strength | 12.2 MPa @Temperature 75.0 °C | 1770 psi @Temperature 167 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | ||
| 28.9 MPa @Temperature 0.000 °C | 4190 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| 41.9 MPa @Temperature 25.0 °C | 6080 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 7.90e+7 ohm-cm @Temperature 150 °C | 7.90e+7 ohm-cm @Temperature 302 °F | cured 2 hours @ 93°C | ||
| 7.70e+8 ohm-cm @Temperature 112 °C | 7.70e+8 ohm-cm @Temperature 234 °F | cured 2 hours @ 93°C | |||
| 2.70e+9 ohm-cm @Temperature 100 °C | 2.70e+9 ohm-cm @Temperature 212 °F | cured 2 hours @ 93°C | |||
| 9.40e+14 ohm-cm @Temperature 25.0 °C | 9.40e+14 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 22 min @Temperature 25.0 °C | 22 min @Temperature 77.0 °F | 200 g | ||
| Gel Time | 6.00 min @Temperature 93.0 °C | 6.00 min @Temperature 199 °F | 10 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 10.2 | AboCure 8110-1 | |||
| 100 | AboCast 8110-6 | ||||