- 吸水率 [%]: 0.26
- 弯曲强度 [MPa]: 50.33
Physical Properties | Metric | English | Comments |
---|---|---|---|
Water Absorption | 0.26 % | 0.26 % | in 24 hours. |
Viscosity Measurement | 1200 | 1200 | |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 81 | 81 | |
Tensile Strength, Ultimate | 50.33 MPa | 7300 psi | |
Elongation at Break | 4.5 % | 4.5 % | |
Flexural Strength | 93.77 MPa | 13600 psi | |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 8.00e+10 ohm-cm @Temperature 93.3 °C | 8.00e+10 ohm-cm @Temperature 200 °F | |
5.00e+12 ohm-cm @Temperature 65.6 °C | 5.00e+12 ohm-cm @Temperature 150 °F | ||
4.00e+15 ohm-cm @Temperature 25.0 °C | 4.00e+15 ohm-cm @Temperature 77.0 °F | ||
Dielectric Constant | 3.36 @Frequency 1e+6 Hz | 3.36 @Frequency 1e+6 Hz | |
Dissipation Factor | 0.013 @Frequency 1e+6 Hz | 0.013 @Frequency 1e+6 Hz | |
Processing Properties | Metric | English | Comments |
Processing Temperature | 25.0 °C | 77.0 °F | Curing time: 3 weeks |