- 缺口冲击强度: 0.24
- 断裂伸长率 [%]: 112.7
- 弯曲强度 [MPa]: 78.46
- 弯曲模量 [MPa]: 2.48
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 100 @Temperature 70.0 °C | 100 @Temperature 158 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 101 | 101 | |||
| Tensile Strength, Ultimate | 78.46 MPa | 11380 psi | |||
| Elongation at Break | 8.5 % | 8.5 % | |||
| Flexural Yield Strength | 112.7 MPa | 16350 psi | |||
| Flexural Modulus | 2.48 GPa | 360 ksi | |||
| Compressive Yield Strength | 107.6 MPa | 15610 psi | |||
| Compressive Modulus | 1.87 GPa | 271 ksi | |||
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | >= 1.24e+16 ohm-cm | >= 1.24e+16 ohm-cm | |||
| Surface Resistance | 3.53e+15 ohm | 3.53e+15 ohm | |||
| Dielectric Constant | 3.55 @Frequency 1e+6 Hz | 3.55 @Frequency 1e+6 Hz | |||
| 4.01 @Frequency 1000 Hz | 4.01 @Frequency 1000 Hz | ||||
| 4.06 @Frequency 60 Hz | 4.06 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0047 @Frequency 60 Hz | 0.0047 @Frequency 60 Hz | |||
| 0.012 @Frequency 1000 Hz | 0.012 @Frequency 1000 Hz | ||||
| 0.037 @Frequency 1e+6 Hz | 0.037 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 123 °C | 253 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 29 min | 29 min | 500 g at 70°C | ||
| Descriptive Properties | |||||
| Exotherm | 270°C | Peak | |||