- 缺口冲击强度: 0.235
- 断裂伸长率 [%]: 83.91
- 弯曲强度 [MPa]: 46.95
- 弯曲模量 [MPa]: 2.25
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 4000 - 6000 cP | 4000 - 6000 cP | 50-6 | ||
| 14000 - 20000 cP | 14000 - 20000 cP | 50-1 | |||
| 6500 cP @Temperature 25.0 °C | 6500 cP @Temperature 77.0 °F | at 100/35 (50-6/50-1) pbw | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 82 | 82 | |||
| Tensile Strength, Ultimate | 46.95 MPa | 6810 psi | |||
| Elongation at Break | 2.0 % | 2.0 % | |||
| Flexural Yield Strength | 83.91 MPa | 12170 psi | |||
| Flexural Modulus | 2.25 GPa | 326 ksi | |||
| Compressive Yield Strength | 84.74 MPa | 12290 psi | |||
| Compressive Modulus | 1.65 GPa | 239 ksi | |||
| Izod Impact, Notched | 0.235 J/cm | 0.440 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 4.86e+15 ohm-cm | 4.86e+15 ohm-cm | |||
| Surface Resistance | 7.85e+15 ohm | 7.85e+15 ohm | |||
| Dielectric Constant | 2.95 @Frequency 1e+6 Hz | 2.95 @Frequency 1e+6 Hz | |||
| 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | ||||
| 3.24 @Frequency 60 Hz | 3.24 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0097 @Frequency 60 Hz | 0.0097 @Frequency 60 Hz | |||
| 0.0097 @Frequency 1000 Hz | 0.0097 @Frequency 1000 Hz | ||||
| 0.021 @Frequency 1e+6 Hz | 0.021 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 92.0 °C | 198 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 160 min | 160 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 153°C | Peak | |||