- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.4
- 断裂伸长率 [%]: 137.9
- 弯曲强度 [MPa]: 68.95
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |
| Water Absorption | 0.40 - 0.50 % | 0.40 - 0.50 % | (60x10X4 mm bar) after 1 hour at 100°C (212°F) |
| 0.50 - 0.60 % | 0.50 - 0.60 % | (60x10X4 mm bar) after 10 days at 20°C (77°F) | |
| Viscosity | 200 - 300 cP @Temperature 60.0 °C | 200 - 300 cP @Temperature 140 °F | |
| 1000 - 2000 cP @Temperature 40.0 °C | 1000 - 2000 cP @Temperature 104 °F | ||
| 20000 - 40000 cP @Temperature 21.0 °C | 20000 - 40000 cP @Temperature 69.8 °F | ||
| Vapor Pressure | <= 0.0000133 bar | <= 0.0100 torr | AboCure, at 20°C |
| 0.00133 bar | 1.00 torr | AboCast, at 180°C | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 68.95 MPa | 10000 psi | |
| Modulus of Elasticity | 2.758 GPa | 400.0 ksi | |
| Flexural Yield Strength | 137.9 MPa | 20000 psi | |
| Compressive Yield Strength | 124.1 MPa | 18000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.50e+16 ohm-cm | >= 1.50e+16 ohm-cm | |
| Dielectric Constant | 3.7 - 4.2 @Frequency 1e+6 Hz | 3.7 - 4.2 @Frequency 1e+6 Hz | |
| 4.0 - 4.5 @Frequency 1000 Hz | 4.0 - 4.5 @Frequency 1000 Hz | ||
| 4.1 - 4.5 @Frequency 50 Hz | 4.1 - 4.5 @Frequency 50 Hz | ||
| Dielectric Strength | 15.7 - 17.7 kV/mm @Thickness 3.17 mm | 400 - 450 kV/in @Thickness 0.125 in | Short time value |
| Dissipation Factor | 0.0050 - 0.0070 @Frequency 1000 Hz | 0.0050 - 0.0070 @Frequency 1000 Hz | |
| 0.020 - 0.040 @Frequency 1e+6 Hz | 0.020 - 0.040 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 - 70.0 µm/m-°C @Temperature 20.0 °C | 33.3 - 38.9 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.130 - 0.170 W/m-K | 0.902 - 1.18 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 160 °C | 320 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Pot Life | 60 - 120 min | 60 - 120 min | at 60°C (140°F) |
| 180 - 300 min | 180 - 300 min | at 40°C (104°F) | |
| 420 - 600 min | 420 - 600 min | 20°C (68°F) | |