- 弯曲强度 [MPa]: 41.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 19000 cP | 19000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 77 | 77 | |||
| Tensile Strength, Ultimate | 41.7 MPa | 6050 psi | after optimum cure | ||
| Elongation at Break | 2.1 % | 2.1 % | |||
| Adhesive Bond Strength | 49.0 MPa | 7100 psi | Steel-Steel; after optimum cure | ||
| 15.9 MPa @Temperature -54.4 °C | 2300 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 20.0 MPa @Temperature 82.2 °C | 2900 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 27.6 MPa @Temperature 25.0 °C | 4000 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 46.0 µm/m-°C @Temperature 20.0 °C | 25.6 µin/in-°F @Temperature 68.0 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Glass Transition Temp, Tg | 118 °C | 244 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 22.2 °C | 72.0 °F | Room Temp Cure Possible | ||
| 98.9 °C | 210 °F | Optimum cure is 2 hr. @ 210°F | |||
| 149 °C | 300 °F | Fast cure is 5 min. @ 300°F | |||
| Pot Life | 150 min | 150 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Grey | ||||
| Mix Ratio | 5/2 | By Weight | |||