- 弯曲强度 [MPa]: 46.9
- 弯曲模量 [MPa]: 6.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 89 @Temperature 25.0 °C | 89 @Temperature 77.0 °F | |||
| Tensile Strength, Ultimate | 46.9 MPa | 6800 psi | |||
| Flexural Strength | 61.4 MPa | 8900 psi | |||
| Flexural Modulus | 6.62 GPa | 960 ksi | |||
| Compressive Strength | 90.3 MPa | 13100 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.9 °C | 138 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 480 - 720 min @Temperature 24.0 °C | 8.00 - 12.0 hour @Temperature 75.2 °F | |||
| Pot Life | 18 - 22 min @Temperature 24.0 °C | 18 - 22 min @Temperature 75.2 °F | 4 oz. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 6:1 by weight, 4:1 by volume, resin/harder | ||||
| Mixed Viscosity, Brookfield | Thixotropic | ||||